| C % | Mo% | Cr% | P% | S% | Fe % |
| 0.2 - 0.4 | 0.4 - 0.6 | 1.0 - 1.2 | ≦0.002 | ≦0.002 | Bal. |
| Parameter | Unit | Typical Value | Reference Range | Testing Method |
| Melt Index | g/10min | 200 | 150 - 300 | ISO 1133 (190 ℃, 21.6Kg) |
| Green Density | g/cm³ | 5.10 | 5.08 - 5.12 | ISO 3369 |
| Sintered Density | g/cm³ | 7.70 | 7.60 - 7.80 | ISO 3369 |
| Mold Factor | 1.190 | 1.185 - 1.195 | Mold Dimension / Product Dimension |
| Sintered State | Thermally Treated State | Thermally Treated State | |
| Density | ≥7.70g/cm³ | ||
| Yield Strength | ≥300MPa | ≥900 MPa | ≥1100 MPa |
| Tensile Strength | ≥400MPa | ≥1000 MPa | ≥1300 MPa |
| Elongation | ≥5% | ≥3% | ≥2 % |
| Impact Value | ≥50J/m² | ||
| Hardness | 130 - 190 HV10 | ≥350 HV10 (35HRC) | ≥650 HV10 (55HRC) |
An advanced through - hardened versatile material. It's used in automotive parts, mechanical engineering, etc. Parts of this grade sintered in pure hydrogen can also be used as soft magnetic materials parts of similar grades.